Oliver Heiml, Gerhard Gritzner,
"Polycrystalline (Tl0.5Pb0.5)(Sr0.9Ba0.1)2Ca2Cu3Oy superconducting thick films with high critical current densities"
, in Superconductor Science and Technology, Vol. 15, Seite(n) 956- 959, 6-2002, ISSN: 0953-2048, Polycrystalline (Tl0.5Pb0.5)(Sr0.9Ba0.1)2Ca2Cu3Oy superconducting thick films with high critical current densities, Oliver Heiml and Gerhard Gritzner, Superconductor Science and Technology, 15 (2002) 956 - 959
Original Titel:
Polycrystalline (Tl0.5Pb0.5)(Sr0.9Ba0.1)2Ca2Cu3Oy superconducting thick films with high critical current densities
Sprache des Titels:
Englisch
Original Kurzfassung:
Superconducting (Tl0.5Pb0.5)(Sr0.9Ba0.1)2Ca2Cu3Oy films were fabricated on lanthanum aluminate substrates by screen printing of the precursor material followed by ex situ thallination. The thickness of the films varied between 1.3 and 2.6 ?m. X-ray diffraction and optical microscopy showed that the films were highly textured. Samples with critical temperatures Tc(0) between 116 and 120 K and with transition widths ÄT(90-10%) of 1 K have been fabricated. Critical current densities between 0.6 and 0.9 MA cm-2 were measured.
Sprache der Kurzfassung:
Englisch
Journal:
Superconductor Science and Technology
Volume:
15
Seitenreferenz:
956- 959
Erscheinungsmonat:
6
Erscheinungsjahr:
2002
Notiz zum Zitat:
Polycrystalline (Tl0.5Pb0.5)(Sr0.9Ba0.1)2Ca2Cu3Oy superconducting thick films with high critical current densities, Oliver Heiml and Gerhard Gritzner, Superconductor Science and Technology, 15 (2002) 956 - 959
Forschungs-