"Tl-1223 Thick Films - A Competitor for Coated Conductors?"
, in S. Toenies, H.W. Weber, G. Gritzner, O. Heiml and M. Eder, in IEEE Transactions on Applied Superconductivity, Vol. 13, Seite(n) 2618 - 2621, 2003
Original Titel:
Tl-1223 Thick Films - A Competitor for Coated Conductors?
Sprache des Titels:
Englisch
Original Kurzfassung:
Tl-1223 thick films were grown on single crystalline LaAlO3 substrates by a screen printing method and doped with small amounts of 235U. The critical current density was measured by dc transport measurements in fields up to 15 T and at temperatures between 30 K and 85 K. Furthermore, the angular dependence of the critical current density and of the irreversibility lines were studied. Excellent texture and very high critical current densities with a weak field dependence were found in the as grown samples. Substantial enhancements of the critical current density and enhanced irreversibility lines are observed after thermal and fast neutron irradiation. The weak field dependence of Jc is further reduced. The results are compared with YBaCuO coated conductors and Bi-2223 tapes.
Sprache der Kurzfassung:
Englisch
Englischer Titel:
Tl-1223 Thick Films - A Competitor for Coated Conductors?
Englische Kurzfassung:
Tl-1223 thick films were grown on single crystalline LaAlO3 substrates by a screen printing method and doped with small amounts of 235U. The critical current density was measured by dc transport measurements in fields up to 15 T and at temperatures between 30 K and 85 K. Furthermore, the angular dependence of the critical current density and of the irreversibility lines were studied. Excellent texture and very high critical current densities with a weak field dependence were found in the as grown samples. Substantial enhancements of the critical current density and enhanced irreversibility lines are observed after thermal and fast neutron irradiation. The weak field dependence of Jc is further reduced. The results are compared with YBaCuO coated conductors and Bi-2223 tapes.
Journal:
IEEE Transactions on Applied Superconductivity
Volume:
13
Seitenreferenz:
2618 - 2621
Erscheinungsjahr:
2003
Notiz zur Publikation:
Tl-1223 Thick Films – A Competitor for Coated Conductors?
S. Toenies, H.W. Weber, G. Gritzner, O. Heiml and M. Eder
IEEE Transactions on Applied Superconductivity, 13 (2003) 2618 - 2621
Forschungs-