Textured nickel tapes prepared from commercially available material
Sprache des Titels:
Englisch
Original Kurzfassung:
Textured Ni tapes were fabricated from commercially available nickel pellets (98.5% Ni). Ingots produced by a melt process were cold rolled to 150 – 400 μm thick tapes. Texturing was achieved by annealing in a reducing atmosphere (Ar + 6.5% v/v H2). Sharp cubic biaxial textured Ni tapes were obtained by thermal treatment at 1000°C for 2 hours in a reducing atmosphere. The tapes were characterized by scanning electron microscopy, X-ray diffraction and by electron backscattering diffraction. The tensile strength, the thermal expansion behavior and the Vickers hardness for the cold rolled tapes and for the heat-treated tapes were measured.
Sprache der Kurzfassung:
Englisch
Englischer Titel:
Textured Ni tapes prepared from commercially available material
Englische Kurzfassung:
Textured Ni tapes were fabricated from commercially available nickel pellets (98.5% Ni). Ingots produced by a melt process were cold rolled to 150 – 400 μm thick tapes. Texturing was achieved by annealing in a reducing atmosphere (Ar + 6.5% v/v H2). Sharp cubic biaxial textured Ni tapes were obtained by thermal treatment at 1000°C for 2 hours in a reducing atmosphere. The tapes were characterized by scanning electron microscopy, X-ray diffraction and by electron backscattering diffraction. The tensile strength, the thermal expansion behavior and the Vickers hardness for the cold rolled tapes and for the heat-treated tapes were measured.
Journal:
Central European Journal of Chemistry
Veröffentlicher:
Springer
Volume:
6
Seitenreferenz:
135 - 139
Erscheinungsjahr:
2008
Anzahl der Seiten:
5
Notiz zur Publikation:
Textured Ni tapes prepared from commercially available material
O. Staller, D. Holzmann, G. Gritzner, P. Diko, D. Mikolaj and F. Kovac;
Cent. Eur. J Chem. 6 (2008) 135 - 139 DOI: 10.2478/s11532-008-0013-8